Enameled Aluminum Wire QZL-2/130

  • Street: No. 88, Chuangju Road, Qidu Town, Wujiang, Suzhou Jiangsu Province, China
  • 0.10mm2.00mm155ECW

    Description

    Characteristic: The Enameled Aluminum Wire has excellent properties of mechanical strength .film adhesion and solvent resistance,light weight and flexibility.lt is widely used in transformers,inductors,ballasts.electrial appliances, deflection coils in display,antimagnetized coils,induction cooker,microwave oven,reactor,etc.

    Standard in accordance with : IEC 60317-0-3:2008

    Type: QZL-2/130

    XINYU ELECTRICAL 130 Enameled Aluminum Wire
    PRODUCT: China Enameled Aluminum Wire
    STANDARD:IEC 60317-0-3:2008
    DATE:10th,Jul.,2017
    TYPE:QZL-2/130
    SIZE:1.800mm

    TESTING ITEMS Refer to REQUIREMENT TESTING DATA RESULTS
    1 Appearance IEC 60317-0-3:2008 3.3 Smooth Surface Qualified Qualified
    2 Conductor Dimension IEC 60317-0-3:2008 4.1 1.800±0.018mm 1.799 Qualified
    3 Over-all Diameter IEC 60317-0-3:2008 4.4.1 ≤1.909mm 1.885 Qualified
    4 Minimum Film Thickness IEC 60317-0-3:2008 4.3.1 ≥0.073mm 0.086 Qualified
    5 Elongation IEC 60317-0-3:2008.6 ≥15﹪ 27 Qualified
    6 Electrical Resistance (20℃) IEC 60317-0-3:2008.5 0.0106-0.0113 Ω/m 0.0108 Qualified
    7 Breakdown Voltage (Room Temperature) IEC 60317-0-3:2008.13 ≥ 5.0KV 7.2, 8.0, 7.8, 7.4, 8.5 Qualified
    8 Tensile Strength IEC 60317-0-3:2008.6 ≥ 80 N/mm2 97 Qualified
    9 Tension Test IEC 60317-0-3:2008 8.2 Stretch 15%,
    Coating No Crack No Crack Qualified
    10 Heat Shock IEC 60317-0-3:2008.9 155℃*30min, Coating No Crack (Stretch 15%) No Crack Qualified
    11 Solvent Test IEC 60317-0-3:2008 12 “H” No Crack Qualified
    12 RoHS Confirmation   RoHS Requirement Qualified Qualified

    Enameled wire: http://www.xinyu-enameledwire.com/

    Enameled Aluminum Wire: http://www.xinyu-enameledwire.com/product/enameled-aluminum-wire/

    Listing ID: 8015a52d7f55aa54

    Report problem

    Processing your request, Please wait....